Russian Journal of Inorganic Chemistry, Tập 41,Trang 1349-1672Chemical Society., 1996 |
Từ bên trong sách
Kết quả 1-3 trong 51
Trang 1357
... powder dif- fraction , microstructure observation , and microhard- ness and density measurements . The initial compounds were identified by DTA and X - ray powder analysis . The melting points of Cu2GeTe3 ( 767 K ) and CdTe ( 1360 K ) ...
... powder dif- fraction , microstructure observation , and microhard- ness and density measurements . The initial compounds were identified by DTA and X - ray powder analysis . The melting points of Cu2GeTe3 ( 767 K ) and CdTe ( 1360 K ) ...
Trang 1422
... powder , which seems to be the mixed - valence Pt ( II , IV ) compound [ PtEnCl2 ] [ PtEnCl4 ] . The same bright red powder forms upon grinding an equimolar mixture of yellow crystals of the PtEnCl2 and PtEnCl , diamines . In this powder ...
... powder , which seems to be the mixed - valence Pt ( II , IV ) compound [ PtEnCl2 ] [ PtEnCl4 ] . The same bright red powder forms upon grinding an equimolar mixture of yellow crystals of the PtEnCl2 and PtEnCl , diamines . In this powder ...
Trang 1506
... powder patterns of the alloys ( Fig . 2 ) , and the data in the table . The powder pattern of the metaarsenate is identical to that given in [ 1 ] ; according to [ 1 ] , the compound crys- tallizes in a hexagonal system . A eutectic is ...
... powder patterns of the alloys ( Fig . 2 ) , and the data in the table . The powder pattern of the metaarsenate is identical to that given in [ 1 ] ; according to [ 1 ] , the compound crys- tallizes in a hexagonal system . A eutectic is ...
Nội dung
Vol 41 No 9 | 1349 |
The Cu₂GeTe3CdTe System and the Structure of the Compound Cu₂CdGeTe4 | 1356 |
Ammonium Sodium Tripolyphosphate NH44NaP3O10 4H2O | 1363 |
Bản quyền | |
17 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption according acid activation analysis angles anion appear aqueous atoms band bond calculated cations Chem chemical Chemistry chlorine cm-¹ complex composition compounds concentration containing cooling coordination Copyright corresponding crystals curves decrease dependence determined diagram distances effect electron energy equilibrium experimental fact field formation fraction groups H₂O heating hydrogen increase indicates Inorganic intensity interaction ions Khim layers ligand magnetic measured melting metal method mol/l molecules Moscow Neorg observed obtained occur Original oxidation oxygen atoms parameters patterns peak phase plane positions potassium powder precipitate prepared properties Publishing range ratio reaction REFERENCES region respectively Russian salts samples Sciences shows similar solid solutions solubility solution space group spectra spectrum stable stage structure studied surface synthesis Table temperature thermal tion unit cell values X-ray diffraction