Trang 1243
... ratio SiO2 P205 1.4 : 1 ; b ) initial mixture with molar ratio SiO2 : P2O5 = 1 : 2 ; c ) the compound with the molar ratio SiO2 : P205 1.5-1.6 : 1 . على الله الله Diffraction patterns of phases isolated on heating. Translated from ...
... ratio SiO2 P205 1.4 : 1 ; b ) initial mixture with molar ratio SiO2 : P2O5 = 1 : 2 ; c ) the compound with the molar ratio SiO2 : P205 1.5-1.6 : 1 . على الله الله Diffraction patterns of phases isolated on heating. Translated from ...
Trang 1245
... ratios were kept at various tem- peratures for 1-22 h ( Table 2 ) . Polyphosphoric acid ( 76 to 78 % P2O5 ) was used to intensify the reaction . Mixing poly- phosphoric acid heated to 200 ° C with amorphous silica in the molar ratio ...
... ratios were kept at various tem- peratures for 1-22 h ( Table 2 ) . Polyphosphoric acid ( 76 to 78 % P2O5 ) was used to intensify the reaction . Mixing poly- phosphoric acid heated to 200 ° C with amorphous silica in the molar ratio ...
Trang 1444
... ratios from 15 : 1 to 1 : 1 . Further increase in the ratio to 1 : 15 leads to a decrease in the copre- cipitation at all pH values . Increase in pH to 9 leads to a decrease in coprecipitation at all original component ratios ; the ...
... ratios from 15 : 1 to 1 : 1 . Further increase in the ratio to 1 : 15 leads to a decrease in the copre- cipitation at all pH values . Increase in pH to 9 leads to a decrease in coprecipitation at all original component ratios ; the ...
Nội dung
CONTENTS | 923 |
The thermal decomposition of ZnBr2 2H₂O | 931 |
Preparation of sodium and calcium trivanadates | 940 |
Bản quyền | |
4 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1982 Translated absorption Akad anions aqueous solutions atoms bands bismuth bond boric acid calcium calculated cations Chem chemical Chemistry chloride chromium(III cm-¹ cm¯¹ cm¹ components composition compounds concentration constants containing coordination copper(II corresponding crystallisation crystals curves decrease determined ditto electrons endothermic endothermic effect equilibrium diagram ethanol eutectic experimental Figure formed H₂O heating hydrated hydrogen hydrolysis hydroxide increase infrared spectra Inorg interaction investigation ionic ions isotherm Khim lanthanide lattice parameters ligand mass melting metal method mixture mole molecules Moscow Nauk SSSR Neorg nitrate obtained oxide oxygen peritectic platinum(II potassium present protons Raman range ratio reaction region Russ Russ.J salt shows sodium solid phases solid solutions solid-phase synthesis solubility specimens spectrum structure studied sulphate synthesis temperature thallium thermal decomposition tion Translated from Zhurnal vanadates vanadium vibrations wavenumbers X-ray diffraction X-ray diffraction patterns Zhur Zhur.Neorg Zhurnal Neorganicheskoi Khimii