Trang 1031
The X - ray diffraction pattern of the sample heated to 700 ° C exhibits the peaks of La CuO4 , Cuo , and Nio . Lanthanum oxide presumably formed upon decomposition of La2O2CO3 seems to instantly react with copper oxide , which accounts ...
The X - ray diffraction pattern of the sample heated to 700 ° C exhibits the peaks of La CuO4 , Cuo , and Nio . Lanthanum oxide presumably formed upon decomposition of La2O2CO3 seems to instantly react with copper oxide , which accounts ...
Trang 1071
The X - ray diffraction pattern does not contain any reflections attributable to Gd2W209 . The exothermic peak at 1050 ° C is , apparently , associated with the polymorphous transformation of Gd2W209 , which agrees with the data ...
The X - ray diffraction pattern does not contain any reflections attributable to Gd2W209 . The exothermic peak at 1050 ° C is , apparently , associated with the polymorphous transformation of Gd2W209 , which agrees with the data ...
Trang 1521
The NazEr_F3 ( PO2 ) 2 and NaErFPO4 were found in the X - ray diffraction pattern of NazEr2 ( PO4 ) 3 is rather com- NaF - ErPO , diagonal section ; NasErF2 ( PO ) 2 , in the plex because of the lack of single crystals and structural ...
The NazEr_F3 ( PO2 ) 2 and NaErFPO4 were found in the X - ray diffraction pattern of NazEr2 ( PO4 ) 3 is rather com- NaF - ErPO , diagonal section ; NasErF2 ( PO ) 2 , in the plex because of the lack of single crystals and structural ...
Nội dung mọi người đang nói đến - Viết bài đánh giá
Chúng tôi không t́m thấy bài đánh giá nào ở các vị trí thông thường.
Nội dung
Vol 40 No 7 | 1022 |
Defects of the Unit Cell and Magnetic Ordering | 1035 |
Germanotovanadates of RareEarth Elements LnGeVO | 1043 |
26 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption Academy according acid activity addition analysis angles anion aqueous assigned atoms bands bond calculated cation cell changes Chem chemical Chemistry complexes composition compounds concentration constants containing coordination copper Copyright corresponding crystals curves decomposition decrease dependence described determined distances effect electronic energy equilibrium experimental extraction fact fluoride formation groups heating hydrogen increase indicates initial Inorganic Institute intensity interaction ions Khim ligand lines melting metal method mixture molecules Moscow Neorg Note observed obtained occurs oxides oxygen parameters pattern phase points position powder prepared presents pressure properties Publishing range ratio reaction REFERENCES region respectively Russian salts samples Sciences shift shows signals similar solid solubility solutions spectra spectrum stability structure studied synthesis Table temperature thermal tion Translation values vibrations X-ray diffraction