Russian Journal of Inorganic Chemistry, Tập 42,Trang 1449-1974Chemical Society., 1997 |
Từ bên trong sách
Kết quả 1-3 trong 28
Trang 1463
... dependence of magnetoresistance for La0.60Y0.07Ca0.33MnO3 samples annealed at 1200 ° C in O2 flow for ( 1 ) 6 , ( 2 ) 12 , ( 3 ) 18 , and ( 4 ) 80 h . relatively high ( Fig . 2 ) , about 55 % at 250 K , and depends on the duration of ...
... dependence of magnetoresistance for La0.60Y0.07Ca0.33MnO3 samples annealed at 1200 ° C in O2 flow for ( 1 ) 6 , ( 2 ) 12 , ( 3 ) 18 , and ( 4 ) 80 h . relatively high ( Fig . 2 ) , about 55 % at 250 K , and depends on the duration of ...
Trang 1486
... dependence of the ( 1 ) weight loss and ( 2-6 ) dehydration degree a of a iron ( III ) oxide hydroxide with the use of different carrier gases : ( 1 , 5 ) N2 ( special - purity grade ) , ( 2 ) moist air ( 2.8 vol % ) , ( 3 ) Ar + CH4 ...
... dependence of the ( 1 ) weight loss and ( 2-6 ) dehydration degree a of a iron ( III ) oxide hydroxide with the use of different carrier gases : ( 1 , 5 ) N2 ( special - purity grade ) , ( 2 ) moist air ( 2.8 vol % ) , ( 3 ) Ar + CH4 ...
Trang 1743
... dependence of calculated parameters on the inclusion of electron correlation . Thus , in contrast to the triplet LiNO ( T ) and LiPS ( T ) molecules , in which cyclic structures remain isomers of 3 , planar bicyclic structure 3 , in ...
... dependence of calculated parameters on the inclusion of electron correlation . Thus , in contrast to the triplet LiNO ( T ) and LiPS ( T ) molecules , in which cyclic structures remain isomers of 3 , planar bicyclic structure 3 , in ...
Nội dung
First International Workshop Sulfurous Compounds and the Environment | 1448 |
Vol 42 No 10 | 1449 |
Magnetoresistive Manganites La0 67Ca0 33MnO3 and La0 60Y0 07Ca0 33MnO3 | 1461 |
Bản quyền | |
58 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption Academy acid addition analysis angles anions aqueous atoms band bonds calculated cations changes characteristic Chem chemical Chemistry cm-¹ complex components composition compounds concentration constant containing coordination Copyright corresponding crystal structure curve decrease dependence described determined distances effect electronic energy equilibrium experimental formation given H₂O heat hydrogen bonds increase indicate Inorganic Institute intensity interaction ions Khim ligand measured melting metal method molecules Moscow Neorg nitrogen observed obtained occurs Original oxide parameters pattern peak phase plane polyhedra polyhedron positions powder prepared present properties Publishing range ratio reaction REFERENCES refined reflections region respectively Russian salt samples Sciences shifts shows similar solid solutions solubility solution space group spectra spectrum studied synthesis Table temperature thermal tion trans transition Translation unit cell values vibrations