Trang 1367
The thermal study of a stoichiometric ( unheated ) 6 ( NH4 ) 2HPO4 + 10CaCO3 mixture detected three endothermic effects , at 80 , 160 , and 800 ° C , coinciding with extensive mass losses by the specimen . These effects are due to the ...
The thermal study of a stoichiometric ( unheated ) 6 ( NH4 ) 2HPO4 + 10CaCO3 mixture detected three endothermic effects , at 80 , 160 , and 800 ° C , coinciding with extensive mass losses by the specimen . These effects are due to the ...
Trang 1451
The fused specimens were subjected to thermal treatment at 1000 , 1500 , and 1700 ° C for periods of 48-720 h . For convenience of comparison the solid - state synthesis was carried out under the same conditions .
The fused specimens were subjected to thermal treatment at 1000 , 1500 , and 1700 ° C for periods of 48-720 h . For convenience of comparison the solid - state synthesis was carried out under the same conditions .
Trang 1457
Values of the unit - cell parameters , hardness , density , and change in mass of specimens from the fluorite - like solid solution region of the ZrO2 - CaO - Gd2O3 system . Mass loss of case specimens ( heated at solid - stage 1200 ° C ...
Values of the unit - cell parameters , hardness , density , and change in mass of specimens from the fluorite - like solid solution region of the ZrO2 - CaO - Gd2O3 system . Mass loss of case specimens ( heated at solid - stage 1200 ° C ...
Nội dung mọi người đang nói đến - Viết bài đánh giá
Chúng tôi không t́m thấy bài đánh giá nào ở các vị trí thông thường.
Nội dung
Inorganic | 1353 |
Contents | 1376 |
Activation of the solution of copperII oxide in aqueous EDTA solutions by the 1385 2683 | 1385 |
Bản quyền | |
9 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
acid aluminium ammonia analysis angle anions atoms bands bond calculated Chem chemical Chemistry chloride complex formation complexes composition compounds concentration constants containing coordination copper copper(II corresponding crystal crystal structure crystallisation curves decrease dependence described determined diagram dioxide EDTA electronic energy English translation equilibrium experimental Figure formation formed given gives halides heating hydrogen increase indicates influence infrared Inorg INORGANIC ions Khim kinetic ligand manganese(II mass metal method mixture molecular molecules Moscow Neorg observed obtained organic oxide parameters phase positions preparation present properties published range rate of solution reaction respectively salts shows similar solid solubility solution solvate solvents specimens spectra stability structure synthesis Table temperature thermal translation translation in Russ tungsten values vibrational X-ray diffraction