... solution process . Influence of the ammonia concentration . The experimental data on the influence of ammonia and EDTA on the kinetics ( Fig . 1 ) show that the rate of solution of copper ( II ) oxide increases only when ammonia and ...
... solution process . Influence of the ammonia concentration . The experimental data on the influence of ammonia and EDTA on the kinetics ( Fig . 1 ) show that the rate of solution of copper ( II ) oxide increases only when ammonia and ...
Trang 1387
Eqn . ( 4 ) shows that the maximum rate of solution should be observed at CEDTA , max given by 13 CEDTA , max√K , K3 → √2.7 10-2.2.4.10-3 = 8 × 10-3 M , which corresponds to the experimental values of CEDTA , max , 9 × 10-3 M. the ...
Eqn . ( 4 ) shows that the maximum rate of solution should be observed at CEDTA , max given by 13 CEDTA , max√K , K3 → √2.7 10-2.2.4.10-3 = 8 × 10-3 M , which corresponds to the experimental values of CEDTA , max , 9 × 10-3 M. the ...
Trang 1388
Mechanism of the solution of copper ( II ) oxide in ammoniacal solutions of EDTA A detailed analysis of different ... rate of solution : Wi = Wm max ΣCull ECEDTA CNH , a · EC EDTA + b · ECEDTA + C ( 11 ) where a , b , c are constants ...
Mechanism of the solution of copper ( II ) oxide in ammoniacal solutions of EDTA A detailed analysis of different ... rate of solution : Wi = Wm max ΣCull ECEDTA CNH , a · EC EDTA + b · ECEDTA + C ( 11 ) where a , b , c are constants ...
Nội dung
Inorganic | 1353 |
Contents | 1376 |
Activation of the solution of copperII oxide in aqueous EDTA solutions by the 1385 2683 | 1385 |
Bản quyền | |
9 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
acid aluminium ammonia analysis angle anions atoms bands bond calculated Chem chemical Chemistry chloride complex formation complexes composition compounds concentration constants containing coordination copper copper(II corresponding crystal crystal structure crystallisation curves decrease dependence described determined diagram dioxide EDTA electronic energy English translation equilibrium experimental Figure formation formed given gives halides heating hydrogen increase indicates influence infrared Inorg INORGANIC ions Khim kinetic ligand manganese(II mass metal method mixture molecular molecules Moscow Neorg observed obtained organic oxide parameters phase positions preparation present properties published range rate of solution reaction respectively salts shows similar solid solubility solution solvate solvents specimens spectra stability structure synthesis Table temperature thermal translation translation in Russ tungsten values vibrational X-ray diffraction