Dissolving the same weight ( 0.20 g ) of the HTSC ( or copper ( II ) oxide ) in hydrochloric acid solutions showed that the quantity of oxygen liberated depends on the acid concentration ( Table 1 ) .
Dissolving the same weight ( 0.20 g ) of the HTSC ( or copper ( II ) oxide ) in hydrochloric acid solutions showed that the quantity of oxygen liberated depends on the acid concentration ( Table 1 ) .
Trang 1359
0 , Change in the ratio of the concentrations of copper ( I ) and copper ( II ) ions in the solution of copper oxides in hydrochloric acid . The published method with formaldoxime , bathocuproin , and PAR [ 4- ( 2 - pyridylazo ) ...
0 , Change in the ratio of the concentrations of copper ( I ) and copper ( II ) ions in the solution of copper oxides in hydrochloric acid . The published method with formaldoxime , bathocuproin , and PAR [ 4- ( 2 - pyridylazo ) ...
Trang 1388
Mechanism of the solution of copper ( II ) oxide in ammoniacal solutions of EDTA HY A detailed analysis of different kinetic mechanisms suggests the following simplest scheme : > [ > Cuo ( solid ) + Hyża * ( CuOH ; .
Mechanism of the solution of copper ( II ) oxide in ammoniacal solutions of EDTA HY A detailed analysis of different kinetic mechanisms suggests the following simplest scheme : > [ > Cuo ( solid ) + Hyża * ( CuOH ; .
Nội dung mọi người đang nói đến - Viết bài đánh giá
Chúng tôi không t́m thấy bài đánh giá nào ở các vị trí thông thường.
Nội dung
SYNTHESIS AND PROPERTIES OF INORGANIC COMPOUNDS | 1353 |
The solidphase synthesis of hydroxyapatite 1366 2649 | 1366 |
The reaction of molybdenum trioxide with magnesium oxide in water 1379 2673 | 1379 |
Bản quyền | |
10 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
acid aluminium ammonia analysis angle anion aqueous atoms bands bond calculated Chem chemical Chemistry chloride complexes composition compounds concentration constants containing coordination copper copper(II corresponding crystal crystal structure crystallisation curves decrease dependence described determined diagram dissociation effect electronic energy English translation equilibrium experimental Figure formation formed given gives halides heating hydrogen increase indicates influence initial Inorg INORGANIC interaction ions Khim kinetic ligand manganese(II mass measured melt metal method mixture molecular molecules Moscow nitrate nitrogen observed obtained organic oxide oxygen parameters peritectic phase positions potassium precipitation preparation present properties range reaction References region respectively salts shows similar sodium solubility solution solvate solvents specimens spectra spectrum stability structure synthesis Table temperature ternary thermal Translated tungsten values vibrations zinc