Dissolving the same weight ( 0.20 g ) of the HTSC [ or copper ( II ) oxide ] in hydrochloric acid solutions showed that the quantity of oxygen liberated depends on the acid concentration ( Table 1 ) . This indicates that the oxygen is ...
Dissolving the same weight ( 0.20 g ) of the HTSC [ or copper ( II ) oxide ] in hydrochloric acid solutions showed that the quantity of oxygen liberated depends on the acid concentration ( Table 1 ) . This indicates that the oxygen is ...
Trang 1378
Table 1 shows that two ranges in which precipitates form with constant composition can be distinguished in the system . The first range corresponds to mixtures for which NB < 1.00 ; under these conditions , a = 1.00 0.004 and b 1.00 ...
Table 1 shows that two ranges in which precipitates form with constant composition can be distinguished in the system . The first range corresponds to mixtures for which NB < 1.00 ; under these conditions , a = 1.00 0.004 and b 1.00 ...
Trang 1461
Table 6. Atomic coordinates , position multiplicities , and site occupany factors for K2Li1 + 38Y1-8F6 ( 8 = 0.13 ) ... are responsible for the very low values of Veq for the Y , and especially the Li , atoms ( Tables 2 and 3 ) .
Table 6. Atomic coordinates , position multiplicities , and site occupany factors for K2Li1 + 38Y1-8F6 ( 8 = 0.13 ) ... are responsible for the very low values of Veq for the Y , and especially the Li , atoms ( Tables 2 and 3 ) .
Nội dung mọi người đang nói đến - Viết bài đánh giá
Chúng tôi không t́m thấy bài đánh giá nào ở các vị trí thông thường.
Nội dung
Inorganic | 1353 |
Contents | 1376 |
Activation of the solution of copperII oxide in aqueous EDTA solutions by the 1385 2683 | 1385 |
Bản quyền | |
9 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
acid aluminium ammonia analysis angle anions atoms bands bond calculated Chem chemical Chemistry chloride complex formation complexes composition compounds concentration constants containing coordination copper copper(II corresponding crystal crystal structure crystallisation curves decrease dependence described determined diagram dioxide EDTA electronic energy English translation equilibrium experimental Figure formation formed given gives halides heating hydrogen increase indicates influence infrared Inorg INORGANIC ions Khim kinetic ligand manganese(II mass metal method mixture molecular molecules Moscow Neorg observed obtained organic oxide parameters phase positions preparation present properties published range rate of solution reaction respectively salts shows similar solid solubility solution solvate solvents specimens spectra stability structure synthesis Table temperature thermal translation translation in Russ tungsten values vibrational X-ray diffraction