... range from 33.33 to 58 mol % SiO2 by means of oscillation phase analysis and thermal analysis . Precision liquidus temperature data have been obtained on 27 alloys of the system . Nonvariant temperatures have been determined . The ...
... range from 33.33 to 58 mol % SiO2 by means of oscillation phase analysis and thermal analysis . Precision liquidus temperature data have been obtained on 27 alloys of the system . Nonvariant temperatures have been determined . The ...
Trang 926
... range 300-490 K. Sample weights were no more than 800 mg . The error in determination of the sample temperature in DTA was less than 3 K. The electrophysical characteristics of polycrystal- line samples pressed in pellets were ...
... range 300-490 K. Sample weights were no more than 800 mg . The error in determination of the sample temperature in DTA was less than 3 K. The electrophysical characteristics of polycrystal- line samples pressed in pellets were ...
Trang 929
... range 120-390 K. At ~ 360 K , a narrow signal emerges , which reflects the commencement of diffusion of NH ions . Above 420 K , virtually all ammonium ions are involved in dif- fusion . The difference in chemical shift between the ...
... range 120-390 K. At ~ 360 K , a narrow signal emerges , which reflects the commencement of diffusion of NH ions . Above 420 K , virtually all ammonium ions are involved in dif- fusion . The difference in chemical shift between the ...
Nội dung
Vol 49 No 5 | 661 |
Synthesis and Properties of Inorganic Compounds | 669 |
Synthesis and XRay Diffraction Characteristics of MMgDyMn2O6 M Li Na K | 674 |
Bản quyền | |
21 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption according acid activation addition analysis angles anion appear atoms band bond cage calculated carbon cation cell changes charge Chem chemical Chemistry clusters cm-¹ compared complexes composition compounds concentration constants containing coordination Copyright corresponding crystal curves decreases determined distances effect electron energy enthalpy existence experimental extraction formation formed frequencies function groups heating HTSC hydrides hydrogen increase Inorg Inorganic interaction ionic ions Journal Khim layers lengths ligand magnetic materials measured melting metal method mixture mol/l molecules Moscow Neorg observed obtained oxide oxygen parameters phase Physics plane positions prepared presence properties range ratio reaction REFERENCES respectively Russian salt sample Sciences shifts shows similar solid solution space group spectra spectrum stability structure studied symmetry synthesis Table temperature thermal tion transition unit values vibrations