During activation , an exchange reaction rapidly occurs to yield thermally unstable products , from which ZrO2 - Y203 solid solution ( ss ) is formed at 400–500 ° C . Effra 2003 ) . km C. 0:43 act : 31.
During activation , an exchange reaction rapidly occurs to yield thermally unstable products , from which ZrO2 - Y203 solid solution ( ss ) is formed at 400–500 ° C . Effra 2003 ) . km C. 0:43 act : 31.
Trang 750
1 ܬ v 2 * 3 starting components became X - ray amorphous even after 3 min of activation . Figure 1 shows X - ray diffraction patterns for a zirconyl nitrate + yttrium carbonate ( Zr : Y = 3 : 2 ) mixture after activation ( curve a ) ...
1 ܬ v 2 * 3 starting components became X - ray amorphous even after 3 min of activation . Figure 1 shows X - ray diffraction patterns for a zirconyl nitrate + yttrium carbonate ( Zr : Y = 3 : 2 ) mixture after activation ( curve a ) ...
Trang 751
Y , 03 1005 a , nm 0.520 a Х x 2 50 0.515 a superposition of the absorption bands of separately activated components . ... Thus , from the vibrational spectra , it follows that , on one hand , the joint activation products are not ...
Y , 03 1005 a , nm 0.520 a Х x 2 50 0.515 a superposition of the absorption bands of separately activated components . ... Thus , from the vibrational spectra , it follows that , on one hand , the joint activation products are not ...
Nội dung mọi người đang nói đến - Viết bài đánh giá
Chúng tôi không t́m thấy bài đánh giá nào ở các vị trí thông thường.
Nội dung
Vol 49 No 5 | 662 |
Synthesis and XRay Diffraction Characteristics of MMgDyMn206 M Li Na K | 674 |
Synthesis and Crystal Structure | 685 |
Bản quyền | |
20 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption according acid activation addition analysis angles anion appear atoms band bond cage calculated carbon cation cell changes charge Chem chemical Chemistry clusters compared complexes composition compounds concentration constants containing coordination Copyright corresponding crystal curves decreases determined distances effect electron energy enthalpy existence experimental extraction formation formed frequencies function groups heating HTSC hydrides hydrogen increase Inorg Inorganic interaction ionic ions Journal Khim layers lengths ligand magnetic materials measured melting metal method mixture mol/l molecules Moscow Neorg observed obtained oxide oxygen parameters phase Physics plane positions prepared presence properties range ratio reaction REFERENCES respectively Russian salt sample Sciences shifts shows similar solid solution space group spectra spectrum stability structure studied symmetry synthesis Table temperature thermal tion transition unit values vibrations
Thông tin thư mục
| Tiêu đề | Russian Journal of Inorganic Chemistry, Tập 49,Số phát hành 5-7 |
| Cộng tác viên | British Library. Lending Division, Royal Society of Chemistry (Great Britain), Chemical Society (Great Britain) |
| Nhà xuất bản | British Library Lending Division with the cooperation of the Royal Society of Chemistry, 2004 |
| Xuất lời trích dẫn | BiBTeX EndNote RefMan |