... X - ray powder diffraction and metallo- graphic data pointed to the existence of a heterophase region in the concentration range of 20-70 mol % SiP . The alloys with a silicon phosphide content as high as 20 mol % were the SiAs - based ...
... X - ray powder diffraction and metallo- graphic data pointed to the existence of a heterophase region in the concentration range of 20-70 mol % SiP . The alloys with a silicon phosphide content as high as 20 mol % were the SiAs - based ...
Trang 636
... X - ray diffraction , precision IR spectroscopy , and thermal analysis . Table 1. X - Ray diffraction characteristics of A ". Original Russian Text Copyright © 2003 by Chernorukov , Knyazev , Kortikova , Gur'eva . English Translation ...
... X - ray diffraction , precision IR spectroscopy , and thermal analysis . Table 1. X - Ray diffraction characteristics of A ". Original Russian Text Copyright © 2003 by Chernorukov , Knyazev , Kortikova , Gur'eva . English Translation ...
Trang 676
... X - ray pow- der diffraction . LaCsMgMn2O is tetragonal , a = 11.06 Å , c = 22.07 Å , V = 2699.7 Å3 , Vun.cell = 135.0 Å3 , Z = 20 , PX - ray = 6.17 g / cm3 , Ppycn = 6.14 ± 0.03 g / cm3 . The LaCsCaMn2O6 is cubic , a = 10.80 Å , V ...
... X - ray pow- der diffraction . LaCsMgMn2O is tetragonal , a = 11.06 Å , c = 22.07 Å , V = 2699.7 Å3 , Vun.cell = 135.0 Å3 , Z = 20 , PX - ray = 6.17 g / cm3 , Ppycn = 6.14 ± 0.03 g / cm3 . The LaCsCaMn2O6 is cubic , a = 10.80 Å , V ...
Nội dung
Vol 48 No 4 | 455 |
Structure of a HighPressure Hydroxide Ta₂O5 23H₂O | 464 |
Synthesis and Physicochemical Properties | 472 |
Bản quyền | |
15 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption According acid activity analysis angles anion aqueous atoms band bismuth bond calculated cations cell Chem chemical Chemistry cm-¹ complexes composition compounds concentration constants containing coordination Copyright corresponding crystal curve decomposition decrease dependence described determined distribution effect electronic energy equilibrium existence experimental extraction field formation formed function H₂O heating higher hydrogen increases Inorganic intensity interactions ionic ions Journal Khim ligand lines measured metal method mixture mol/l molecules Moscow Neorg observed obtained occurs organic oxide oxygen parameters phase Phys Physics points positions prepared presence properties range ratio reaction REFERENCES refinement region respectively Russian salt samples Sciences shift shows solid solubility solutions solvent space group spectra spectrum stability structure studied surface synthesis Table temperature thermal tion transition unit values X-ray diffraction