... thermal analysis apparatus in an atmosphere of air . The rate of linear increase in tempera- ture was ~ 1 K min1 , the thermal analysis curves were recorded using 80-100 mg specimens , and heated alumina was used as standard . The ...
... thermal analysis apparatus in an atmosphere of air . The rate of linear increase in tempera- ture was ~ 1 K min1 , the thermal analysis curves were recorded using 80-100 mg specimens , and heated alumina was used as standard . The ...
Trang 1613
... thermal decomposition is complete above 600 ° C with the combustion of the carbon residues . The final decomposition product of the halides is zinc oxide . Table 4 shows that the experimentally determined mass loss is greater than the ...
... thermal decomposition is complete above 600 ° C with the combustion of the carbon residues . The final decomposition product of the halides is zinc oxide . Table 4 shows that the experimentally determined mass loss is greater than the ...
Trang 1621
... thermal decomposition showed that water is removed in stages . The thermogram for calcium hexa- hydroxoindate shows ... thermal analysis indicates the following series of transformations : Cas [ In ( OH ) s ] : 320 ° C -2H.O 2Ca ( OH ) ...
... thermal decomposition showed that water is removed in stages . The thermogram for calcium hexa- hydroxoindate shows ... thermal analysis indicates the following series of transformations : Cas [ In ( OH ) s ] : 320 ° C -2H.O 2Ca ( OH ) ...
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1979 Translated absorption bands acid aluminium analysis anion atoms bond calculated Chem chemical Chemistry chloride chromium(III cm-¹ cm¯¹ cm¹ complex formation components composition compounds concentration coordination copper(II corresponding crystallisation crystals curves decomposition decrease determined ditto DMSO electrical conductivity electronic equilibrium ethanol eutectic experimental extraction Figure fluoride formed H₂O heating hydrogen hydroxide increase infrared infrared spectra Inorg interaction investigated ionic ions isothermal kcal Khim lanthanide ligand liquid magnesium manganese(III mass melt metal method mixture molar mole molecules molybdenum Moscow Nauk SSSR neodymium Neorg nickel(II nitrate obtained oxide oxygen parameters precipitate range ratio reaction reagent Russ Russ.J salt shows sodium solid phases solid solutions solubility solvent specimens spectrum stability constants structure studied sulphate synthesis Table temperature thermal tion Translated from Zhurnal vanadium vanadium(III vibrations wavenumbers X-ray diffraction X-ray diffraction patterns ytterbium Zhur Zhur.Neorg Zhurnal Neorganicheskoi Khimii zirconium