Russian Journal of Inorganic Chemistry, Tập 44,Trang 461-995Chemical Society., 1999 |
Từ bên trong sách
Kết quả 1-3 trong 80
Trang 492
... X - ray powder diffrac- tion patterns ( with a DRON - 3 diffractometer , CuKa radiation , rate 0.5 deg / min ) . The high - temperature X - ray diffraction method was also used in the range from room temperature to 1300 ° C ( a high ...
... X - ray powder diffrac- tion patterns ( with a DRON - 3 diffractometer , CuKa radiation , rate 0.5 deg / min ) . The high - temperature X - ray diffraction method was also used in the range from room temperature to 1300 ° C ( a high ...
Trang 923
... X - ray diffraction pattern , the samples containing 30 , 50 , and 60 mol % Cr2Se , were annealed at 630 ° C for 7 days and quenched . The X - ray diffraction data for the quenched samples ( table ) and the construction of the Tammann ...
... X - ray diffraction pattern , the samples containing 30 , 50 , and 60 mol % Cr2Se , were annealed at 630 ° C for 7 days and quenched . The X - ray diffraction data for the quenched samples ( table ) and the construction of the Tammann ...
Trang 955
... XRD , X - ray powder diffraction ; IR , infrared spectroscopy ; VTA , visual thermal analysis ; XRSA , X - ray structure analysis of a single crystal ; c , congruent ; i , incongruent . Table 2. Crystallographic and thermoanalytical ...
... XRD , X - ray powder diffraction ; IR , infrared spectroscopy ; VTA , visual thermal analysis ; XRSA , X - ray structure analysis of a single crystal ; c , congruent ; i , incongruent . Table 2. Crystallographic and thermoanalytical ...
Nội dung
Contents | 463 |
Synthesis and Properties of Inorganic Compounds | 469 |
The Crystal Structure of Indium Perchlorates InH2O6ClO43 and InH2O6ClO43 3H2O | 476 |
Bản quyền | |
18 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption according acid activity addition amount analysis angle anions aqueous atoms band bond calculated cations Chem chemical Chemistry chloride cm-¹ complex components composition compounds concentration constants containing coordination copper Copyright corresponding crystal curve decomposition decrease described determined diagram distances effect electron energy equal experimental extraction formation groups heating higher hydrogen increase indicates Inorganic intensity interaction Journal Khim layer lead ligand measured melting metal method mixture molecules Moscow Neorg observed obtained occurs oxidation oxygen patterns phase positions powder prepared presented properties range ratio reaction REFERENCES region respectively Russian salt samples Sciences shows similar sodium solid solid solutions solubility solution space group spectra spectrum stability structure studied surface synthesis Table temperature thermal tion transition Translation unit cell values X-ray X-ray diffraction