... melting compound K2MoO4 · KF . Secondary separation lines meet at two eutectic points , E , and E2 . Low - melting phases were found , which may have a potential for application , and their crystallization fields were outlined . Table 2 ...
... melting compound K2MoO4 · KF . Secondary separation lines meet at two eutectic points , E , and E2 . Low - melting phases were found , which may have a potential for application , and their crystallization fields were outlined . Table 2 ...
Trang 1774
... melting compound formed in the system In - P . Its melt- ing temperature is 1070 ° C . The compound forms degenerated eutectics with both In and P ( melting tem- peratures are 154 and 603 ° C , respectively ) . According to [ 19 ] , the ...
... melting compound formed in the system In - P . Its melt- ing temperature is 1070 ° C . The compound forms degenerated eutectics with both In and P ( melting tem- peratures are 154 and 603 ° C , respectively ) . According to [ 19 ] , the ...
Trang 1918
... melting temperatures of the following com- pounds are known from literature : Tm ZnBr2 = 394 ° C [ 1 , p . 493 ] ; Tm HgBr2 = 238 ° C [ 1 , p . 506 ] . The com- pounds Cs2ZnBr4 , Cs2HgBr4 , CsHgBr3 , and CsHg , Br , melt congruently at ...
... melting temperatures of the following com- pounds are known from literature : Tm ZnBr2 = 394 ° C [ 1 , p . 493 ] ; Tm HgBr2 = 238 ° C [ 1 , p . 506 ] . The com- pounds Cs2ZnBr4 , Cs2HgBr4 , CsHgBr3 , and CsHg , Br , melt congruently at ...
Nội dung
Vol 38 No 9 | 1335 |
Synthesis and Study of Ca and EuSubstituted YttriumBased 124Type APR 1 2 1994 | 1341 |
SYNTHESIS AND PROPERTIES OF INORGANIC COMPOUNDS | 1350 |
Bản quyền | |
64 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1993 by Interperiodica 1993 by Zhurnal absorption bands acid Acta Akad amphoteric analysis anion atoms binary bismuth bond length calcd calculated cations Chem chemical chromium(III cm-¹ complexes composition concentration COORDINATION COMPOUNDS coordination number copper(II corresponding crystal curve decomposition decrease diagram elements English Translation Copyright enthalpy eutectic experimental force constants formation frequencies H₂O heating hydrazine increase Inorg Inorganic Chemistry interaction ions Khim kJ/mol layer ligand metal method mixture mol/l molecules Moscow Nauk SSSR Neorg nitrate nitrogen atom NMR spectra observed obtained Original Russian Edition oxide oxime oxygen oxygen atoms parameters phase Phys physicochemical platinum(II plexes properties reaction rhodium rhodium(III Russia Received Russian Academy Russian Edition Copyright salts samples solid solutions space group spectrum structure studied synthesis Table temperature ternary tetraphosphorus thermal thermodynamic thermolysis tion values vibrations X-ray diffraction Zhurnal Neorganicheskoi Khimii ZnBr₂