... crystals Bi1.85S11.85 Ca0.8Cu2,000 and Bi2.53Sr1.90Ca0.90 Cu2.000 , of 5 x 5 x 0.1 mm on average and with T , = 87 K , are prepared . The ( 2223 ) phase is IES found as thin layers in the crystals of the ( 2212 ) phase . 1 Conditions ...
... crystals Bi1.85S11.85 Ca0.8Cu2,000 and Bi2.53Sr1.90Ca0.90 Cu2.000 , of 5 x 5 x 0.1 mm on average and with T , = 87 K , are prepared . The ( 2223 ) phase is IES found as thin layers in the crystals of the ( 2212 ) phase . 1 Conditions ...
Trang 4
... crystals , ( 5-10 ) x ( 5-10 ) x ( 0.1-0.2 ) mm ( 2212 ) crystals , ( 5 - 10 ) × ( 5-10 ) x ( 0.1-0.2 ) mm ; ( 2201 ) impurity ( by X - ray diffraction ) Fine crystals , the ( 2212 ) phase and BaBiO3 ( by X - ray diffraction ) 5 6 1-2 ...
... crystals , ( 5-10 ) x ( 5-10 ) x ( 0.1-0.2 ) mm ( 2212 ) crystals , ( 5 - 10 ) × ( 5-10 ) x ( 0.1-0.2 ) mm ; ( 2201 ) impurity ( by X - ray diffraction ) Fine crystals , the ( 2212 ) phase and BaBiO3 ( by X - ray diffraction ) 5 6 1-2 ...
Trang 548
... crystals CaYAl307 : Cr with melilite structure are studied by an X - ray diffraction anal- ysis . These crystals exhibit intense Cr ++ luminescence , comparable in magnitude to the luminescence of garnet Y3Al5O12 : Cr ++ . The joint ...
... crystals CaYAl307 : Cr with melilite structure are studied by an X - ray diffraction anal- ysis . These crystals exhibit intense Cr ++ luminescence , comparable in magnitude to the luminescence of garnet Y3Al5O12 : Cr ++ . The joint ...
Nội dung
Interaction of Lithium Borohydride with Lithium Hydroxide | 6 |
Synthesis and Thermal Decomposition of the Aluminum Hydroxide Intercalation Compounds | 18 |
The Synthesis and Properties | 28 |
Bản quyền | |
27 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption according acid addition analysis angles anion atoms band bismuth bond calculated cations Chem chemical Chemistry cm-¹ complexes components composition compounds concentration constants containing coordination Copyright corresponding crystals curves decomposition decrease dependence described determined diagram distances effect electron energy equation equilibrium experimental experiments fact formation given H₂O heating hydrogen increase indicates initial Inorganic intensity interaction ions Khim ligand liquidus measured melting metal method mixture mol/l molecules Moscow Neorg observed obtained occurs oxide oxygen parameters peritectic phase positions possible powder diffraction prepared present properties Publishing range ratio reaction REFERENCES region respectively Russian salts samples Sciences shows similar sodium solubility solutions space group spectra spectrum stability structure studied surface synthesis Table temperature thermal tion Translation values X-ray powder