... titanium ( IV ) and zirco- nium ( IV ) oxohydroxide hydrogels freshly precipitated at pH 5.5-12 and xerogels prepared by aging these hydrogels in sodium chloride or sodium sulfate solutions under heating . Thermoanalytical curves and ...
... titanium ( IV ) and zirco- nium ( IV ) oxohydroxide hydrogels freshly precipitated at pH 5.5-12 and xerogels prepared by aging these hydrogels in sodium chloride or sodium sulfate solutions under heating . Thermoanalytical curves and ...
Trang 1287
... titanium ( IV ) its value is far higher . The same concerns to the residual anions of the starting salt . The residual anions decrease to insignifi- cant amounts as a result of aging in electrolyte solu- tions , as in the tervalent ...
... titanium ( IV ) its value is far higher . The same concerns to the residual anions of the starting salt . The residual anions decrease to insignifi- cant amounts as a result of aging in electrolyte solu- tions , as in the tervalent ...
Trang 1288
... Titanium ( IV ) oxohydroxide xerogels ( Table 2 ) are less hydrated than zirconium ( IV ) oxohydroxides ; the dominant composition is TiO ( OH ) 2 . In zirconium oxohydroxide gels ( Table 3 ) prepared from zirconyl nitrate , Zr ( OH ) ...
... Titanium ( IV ) oxohydroxide xerogels ( Table 2 ) are less hydrated than zirconium ( IV ) oxohydroxides ; the dominant composition is TiO ( OH ) 2 . In zirconium oxohydroxide gels ( Table 3 ) prepared from zirconyl nitrate , Zr ( OH ) ...
Nội dung
Vol 48 No 9 | 1282 |
Simultaneous English language translation of the journal is available from MAIK NaukaInterperiodica Russia | 1446 |
Vol 48 No 11 2003 | 1615 |
26 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid Akad analysis angles anion aqueous atoms band bond lengths calculated cations chelate Chem chemical cm-¹ complexes composition compounds concentration coordination Cr₂Se3 crystal structure Crystallogr curves decomposition decreases diastereomers electron English Translation Copyright enthalpy equilibrium europium europium(III experimental formation formed H₂O hydrogen bonds increases Inorganic Chemistry interaction ions Khim kJ/mol layer ligand lithium MAIK Nauka/Interperiodica melting metal method mixture mol/l Moscow Nauk Neorg octahedra Original Russian Text oxidation oxygen atoms phase diagram Phys Physicochemical plexes properties protons Raman range reaction region Russia Received Russian Academy Russian Journal Russian Text Copyright salt samples single crystals sodium solid solutions solubility solvent sorbent space group spectra spectroscopy spectrum spinel SSUS studied Synthesis Table temperature ternary thermal tion trans transition unit cell unit cell parameters values vibrations water molecules whitlockite X-ray diffraction zirconium