Trang 1560
... melting points and melting characters for compounds existing in this system have been refined . The composition of crystallizing phases and compounds is affected by the thermal history of samples . Table 1. Phase - equilibrium ...
... melting points and melting characters for compounds existing in this system have been refined . The composition of crystallizing phases and compounds is affected by the thermal history of samples . Table 1. Phase - equilibrium ...
Trang 1565
... melting point . Fur- ther heating at 0.1-5 K entailed melting of the a - phase . This result was reproduced even when the sample was heated to 1200 ° C , a temperature 450 ° C above the melt- ing point . This might be taken as evidence ...
... melting point . Fur- ther heating at 0.1-5 K entailed melting of the a - phase . This result was reproduced even when the sample was heated to 1200 ° C , a temperature 450 ° C above the melt- ing point . This might be taken as evidence ...
Trang 1566
... melting point of 732 ° C and can undergo metastable peritectic melting to sodium tetraborate Na2O · 4B2O3 and a liquid contain- ing about 73 % boron oxide ( Figs . 1 , 2 ; Table 2 ) at 722 ° C . This result is in fair agreement with ...
... melting point of 732 ° C and can undergo metastable peritectic melting to sodium tetraborate Na2O · 4B2O3 and a liquid contain- ing about 73 % boron oxide ( Figs . 1 , 2 ; Table 2 ) at 722 ° C . This result is in fair agreement with ...
Nội dung
Vol 48 No 9 | 1282 |
Simultaneous English language translation of the journal is available from MAIK NaukaInterperiodica Russia | 1446 |
Vol 48 No 11 2003 | 1615 |
26 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid Akad analysis angles anion aqueous atoms band bond lengths calculated cations chelate Chem chemical cm-¹ complexes composition compounds concentration coordination Cr₂Se3 crystal structure Crystallogr curves decomposition decreases diastereomers electron English Translation Copyright enthalpy equilibrium europium europium(III experimental formation formed H₂O hydrogen bonds increases Inorganic Chemistry interaction ions Khim kJ/mol layer ligand lithium MAIK Nauka/Interperiodica melting metal method mixture mol/l Moscow Nauk Neorg octahedra Original Russian Text oxidation oxygen atoms phase diagram Phys Physicochemical plexes properties protons Raman range reaction region Russia Received Russian Academy Russian Journal Russian Text Copyright salt samples single crystals sodium solid solutions solubility solvent sorbent space group spectra spectroscopy spectrum spinel SSUS studied Synthesis Table temperature ternary thermal tion trans transition unit cell unit cell parameters values vibrations water molecules whitlockite X-ray diffraction zirconium