Melting Solid - state decomposition Eutectic Metastable eutectic Melting Eutectic Solid - state decomposition Metastable eutectic Metastable eutectic Melting Eutectic Melting mol % Fig . 1. Phase diagram for the Na2O. Table 2. Invariant ...
Melting Solid - state decomposition Eutectic Metastable eutectic Melting Eutectic Solid - state decomposition Metastable eutectic Metastable eutectic Melting Eutectic Melting mol % Fig . 1. Phase diagram for the Na2O. Table 2. Invariant ...
Trang 1565
... melting point . Fur- ther heating at 0.1–5 K entailed melting of the a - phase . This result was reproduced even when the sample was heated to 1200 ° C , a temperature 450 ° C above the melt- ing point . This might be taken as evidence ...
... melting point . Fur- ther heating at 0.1–5 K entailed melting of the a - phase . This result was reproduced even when the sample was heated to 1200 ° C , a temperature 450 ° C above the melt- ing point . This might be taken as evidence ...
Trang 1566
... melting point of 732 ° C and can undergo metastable peritectic melting to sodium tetraborate Na2O 4B2O3 and a liquid contain- ing about 73 % boron oxide ( Figs . 1 , 2 ; Table 2 ) at 722 ° C . This result is in fair agreement with the ...
... melting point of 732 ° C and can undergo metastable peritectic melting to sodium tetraborate Na2O 4B2O3 and a liquid contain- ing about 73 % boron oxide ( Figs . 1 , 2 ; Table 2 ) at 722 ° C . This result is in fair agreement with the ...
Nội dung
Vol 48 No 9 | 1282 |
Simultaneous English language translation of the journal is available from MAIK NaukaInterperiodica Russia | 1446 |
Vol 48 No 11 2003 | 1615 |
26 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid activation analysis angles anion atoms band bond calculated cations Chem chemical Chemistry cm-¹ complexes components composition compounds concentration constant containing coordination Copyright corresponding crystal crystal structure curves decreases determined diagram distances effect electron energy experimental field formation formed function heating hydrogen increases Inorganic intensity interaction ions Journal Khim layer ligand materials measured melting metal method mixture molecules Moscow Neorg Note observed obtained oxidation oxygen parameters phase Physics positions prepared properties range ratio reaction REFERENCES refined reflections region respectively ring Russian salt samples Sciences shifts shown shows signals single sodium solid solid solutions solubility solutions space space group spectra spectrum spinel stability structure studied Synthesis Table temperature thermal tion trans transition Translation values vibrations X-ray diffraction