Russian Journal of Inorganic Chemistry, Tập 48,Số phát hành 9-12Chemical Society., 2003 |
Từ bên trong sách
Kết quả 1-3 trong 71
Trang 1610
... layers treated with these solutions corre- spond to PbS diffraction patterns . When PbS layers are treated with alkali solutions containing K3 [ Fe ( CN ) 6 ] , PbO2 does form ( the electrical resistance of the layer decreases ) , but ...
... layers treated with these solutions corre- spond to PbS diffraction patterns . When PbS layers are treated with alkali solutions containing K3 [ Fe ( CN ) 6 ] , PbO2 does form ( the electrical resistance of the layer decreases ) , but ...
Trang 1611
... layer after treat- ing the layer with a Na2S2Og solution . Figure 1 makes it clear that when the oxidizer con- centration is less than 0.2 mol / l , chemical oxidation to PbO2 does not occur , but the PbS layer is destroyed . Likely ...
... layer after treat- ing the layer with a Na2S2Og solution . Figure 1 makes it clear that when the oxidizer con- centration is less than 0.2 mol / l , chemical oxidation to PbO2 does not occur , but the PbS layer is destroyed . Likely ...
Trang 1612
... layer , presumably , as a result of a redox reaction = PbS + PbO2 + 4NaOH Na2PbO2 + Na2PbO3 + H2S + H2O . ( 5 ) This reaction produces easily soluble lead compounds and hydrogen sulfide ; the latter is easily identified by its smell ...
... layer , presumably , as a result of a redox reaction = PbS + PbO2 + 4NaOH Na2PbO2 + Na2PbO3 + H2S + H2O . ( 5 ) This reaction produces easily soluble lead compounds and hydrogen sulfide ; the latter is easily identified by its smell ...
Nội dung
Vol 48 No 9 | 1282 |
Simultaneous English language translation of the journal is available from MAIK NaukaInterperiodica Russia | 1446 |
Vol 48 No 11 2003 | 1615 |
26 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid Akad analysis angles anion aqueous atoms band bond lengths calculated cations chelate Chem chemical cm-¹ complexes composition compounds concentration coordination Cr₂Se3 crystal structure Crystallogr curves decomposition decreases diastereomers electron English Translation Copyright enthalpy equilibrium europium europium(III experimental formation formed H₂O hydrogen bonds increases Inorganic Chemistry interaction ions Khim kJ/mol layer ligand lithium MAIK Nauka/Interperiodica melting metal method mixture mol/l Moscow Nauk Neorg octahedra Original Russian Text oxidation oxygen atoms phase diagram Phys Physicochemical plexes properties protons Raman range reaction region Russia Received Russian Academy Russian Journal Russian Text Copyright salt samples single crystals sodium solid solutions solubility solvent sorbent space group spectra spectroscopy spectrum spinel SSUS studied Synthesis Table temperature ternary thermal tion trans transition unit cell unit cell parameters values vibrations water molecules whitlockite X-ray diffraction zirconium