... glass - formation fields of the Al2 ( SO4 ) 2 - HIO3 - H2O system have been deter- mined . The glass - forming ability , crystallization resistance , and thermal properties for test samples have been studied . A glass - formation ...
... glass - formation fields of the Al2 ( SO4 ) 2 - HIO3 - H2O system have been deter- mined . The glass - forming ability , crystallization resistance , and thermal properties for test samples have been studied . A glass - formation ...
Trang 1440
RESULTS AND DISCUSSION Figure 1 depicts the glass - formation boundaries for the Al2 ( SO4 ) 3 - HIO3 - H2O system . The first glass - forma- tion field extends from the Al2 ( SO4 ) 3 — H2O binary to the HIO - H2O binary . This is a ...
RESULTS AND DISCUSSION Figure 1 depicts the glass - formation boundaries for the Al2 ( SO4 ) 3 - HIO3 - H2O system . The first glass - forma- tion field extends from the Al2 ( SO4 ) 3 — H2O binary to the HIO - H2O binary . This is a ...
Trang 1931
where the tendency to glass formation in the PbX2- AgX - CsX - CdX2 ( X = Cl , Br ) systems was studied but where this supposition was not confirmed because of the absence of phase diagrams . To summarize , glass formation in the CdBr2 ...
where the tendency to glass formation in the PbX2- AgX - CsX - CdX2 ( X = Cl , Br ) systems was studied but where this supposition was not confirmed because of the absence of phase diagrams . To summarize , glass formation in the CdBr2 ...
Nội dung
Vol 48 No 9 | 1282 |
Simultaneous English language translation of the journal is available from MAIK NaukaInterperiodica Russia | 1446 |
Vol 48 No 11 2003 | 1615 |
26 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid activation analysis angles anion atoms band bond calculated cations Chem chemical Chemistry cm-¹ complexes components composition compounds concentration constant containing coordination Copyright corresponding crystal crystal structure curves decreases determined diagram distances effect electron energy experimental field formation formed function heating hydrogen increases Inorganic intensity interaction ions Journal Khim layer ligand materials measured melting metal method mixture molecules Moscow Neorg Note observed obtained oxidation oxygen parameters phase Physics positions prepared properties range ratio reaction REFERENCES refined reflections region respectively ring Russian salt samples Sciences shifts shown shows signals single sodium solid solid solutions solubility solutions space space group spectra spectrum spinel stability structure studied Synthesis Table temperature thermal tion trans transition Translation values vibrations X-ray diffraction