... tetragonal prisms , but X - ray analysis show them to have monoclinic or triclinic sym- metry . The compound is not isomorphous with potassium ( KC1.MgCl2.6H2O ) , rubidium ( RbC1 . MgCl2.6H2O ) or any other carnallite . 1 . N.K. ...
... tetragonal prisms , but X - ray analysis show them to have monoclinic or triclinic sym- metry . The compound is not isomorphous with potassium ( KC1.MgCl2.6H2O ) , rubidium ( RbC1 . MgCl2.6H2O ) or any other carnallite . 1 . N.K. ...
Trang 1075
... tetragonal structure and containing 53.3-53.9 wt . % Cu at 400 ° and 53.6-54.5 wt . % Cu at the eutectic temperature , 548 ° . The phase is formed from the 7 - phase by a peritectic reaction at 591 ° . ( c ) The n - phase ( CuAl ) with ...
... tetragonal structure and containing 53.3-53.9 wt . % Cu at 400 ° and 53.6-54.5 wt . % Cu at the eutectic temperature , 548 ° . The phase is formed from the 7 - phase by a peritectic reaction at 591 ° . ( c ) The n - phase ( CuAl ) with ...
Trang 1297
... tetragonal ) lattice with parameters : a = 6.58 ± ± 0.01 , b = 4.60 ± 0.005 , c = 4.67 , ± 0.005 Å . Taking Z = 2 , the X - ray density is 2.46 ( cf. pyknometric density of a - BeSO , 8 = 2.5 ) . When the lengths of the three crystallo ...
... tetragonal ) lattice with parameters : a = 6.58 ± ± 0.01 , b = 4.60 ± 0.005 , c = 4.67 , ± 0.005 Å . Taking Z = 2 , the X - ray density is 2.46 ( cf. pyknometric density of a - BeSO , 8 = 2.5 ) . When the lengths of the three crystallo ...
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
acid Akad alcohol alkali alloys aluminium ammonia ammonium anion aqueous solution Blagorod bromide cadmium caesium calculated carbonate cerium Chem chemical chloride coefficient complex ion composition concentration copper corresponding cristobalite crystallisation crystals decomposition determined dissociation electrode equilibrium diagram ether ethyl eutectic formation formed gallium glauberite H₂O H₂SO heating curve hydrogen hydroxide increase indium Inorg Inst instability constant ionic strength isotherms K₂SO Khim ligands liquid lithium melting metal method molar ratio molar volumes mole molecules MTPC Na₂SO NaCl Nauk SSSR neodymium Neorg nitrate nitrilotriacetic acid NO₂ Obshch obtained oxide platinum Platiny Drug polyhalite potassium praseodymium precipitate prepared pyridine reaction reagent refractive refractive indices Russ salt saturated shows sodium solid phase solid solutions solubility solvents stability studied sulphate sulphide Table temperature thallium tin selenide tion titanium trans effect uranyl values X-ray Zhur zinc zirconium