Russian Journal of Inorganic Chemistry, Tập 6,Số phát hành 7-12British Library Lending Division with the cooperation of the Royal Society of Chemistry, 1961 |
Từ bên trong sách
Kết quả 1-3 trong 57
Trang 845
... eutectic and limited solid solution ( up to 20 % PbSO ) are formed . The eutectic is at 735 ° and 47 % PbSO . V. G. Berg- man2 showed that there is a separate field for a compound x Na2SO1.y PbSO ,, formed at ~ 680 ° , below the ...
... eutectic and limited solid solution ( up to 20 % PbSO ) are formed . The eutectic is at 735 ° and 47 % PbSO . V. G. Berg- man2 showed that there is a separate field for a compound x Na2SO1.y PbSO ,, formed at ~ 680 ° , below the ...
Trang 1274
... eutectic is formed 2,3 at 26 % C , 3050 ° . The C - Co system . At the eutectic temperature , 1309 ° , cobalt dissolves about 1 % C , decreasing to 0.1 % as the temperature falls . The ( CoC ) eutectic1 contains 2.4 wt . % C. Co - TiC ...
... eutectic is formed 2,3 at 26 % C , 3050 ° . The C - Co system . At the eutectic temperature , 1309 ° , cobalt dissolves about 1 % C , decreasing to 0.1 % as the temperature falls . The ( CoC ) eutectic1 contains 2.4 wt . % C. Co - TiC ...
Trang 1277
... eutectic Co ( cub ) a = 3.556 K3-2 99.8 0.2 ditto ( CoC ) eutectic ( TiC + C ) eutectic Co ( hex ) ditto K2-2 99.4 0.6 K2-1 99.4 0.6 vacuum - melted at 1500 ° K5-1 99.0 1.0 ditto Å Co ( hex ) d ( 101 ) 1.912 * d ( 101 ) 1.910 polygonal ...
... eutectic Co ( cub ) a = 3.556 K3-2 99.8 0.2 ditto ( CoC ) eutectic ( TiC + C ) eutectic Co ( hex ) ditto K2-2 99.4 0.6 K2-1 99.4 0.6 vacuum - melted at 1500 ° K5-1 99.0 1.0 ditto Å Co ( hex ) d ( 101 ) 1.912 * d ( 101 ) 1.910 polygonal ...
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
acid Akad alcohol alkali alloys aluminium ammonia ammonium anion aqueous solution Blagorod bromide cadmium caesium calculated carbonate cerium Chem chemical chloride coefficient complex ion composition concentration copper corresponding cristobalite crystallisation crystals decomposition determined dissociation electrode equilibrium diagram ether ethyl eutectic formation formed gallium glauberite H₂O H₂SO heating curve hydrogen hydroxide increase indium Inorg Inst instability constant ionic strength isotherms K₂SO Khim ligands liquid lithium melting metal method molar ratio molar volumes mole molecules MTPC Na₂SO NaCl Nauk SSSR neodymium Neorg nitrate nitrilotriacetic acid NO₂ Obshch obtained oxide platinum Platiny Drug polyhalite potassium praseodymium precipitate prepared pyridine reaction reagent refractive refractive indices Russ salt saturated shows sodium solid phase solid solutions solubility solvents stability studied sulphate sulphide Table temperature thallium tin selenide tion titanium trans effect uranyl values X-ray Zhur zinc zirconium