Trang 834
... alloys decreases as the Ag concentra- tion rises ( Fig . 4a ) . The hardness of the alloys quenched from 1200 ° passes through a clearly defined maximum ; this is presumably due to age - hardening since the alloy lies near the boundary ...
... alloys decreases as the Ag concentra- tion rises ( Fig . 4a ) . The hardness of the alloys quenched from 1200 ° passes through a clearly defined maximum ; this is presumably due to age - hardening since the alloy lies near the boundary ...
Trang 835
... alloys . The transforma- tion from the homogeneous into the heterogeneous region is not shown . The maximum on the hardness curve is attri- butable to the alloy Ag 5 , Pd 80 , Rh 15 wt . % , which lies near the boundary of the ß - solid ...
... alloys . The transforma- tion from the homogeneous into the heterogeneous region is not shown . The maximum on the hardness curve is attri- butable to the alloy Ag 5 , Pd 80 , Rh 15 wt . % , which lies near the boundary of the ß - solid ...
Trang 885
... alloys containing up to 5 wt . % Gd , which had been forged at 800 ° -900 ° into square 5 x5 mm rods . The addition of up to 3 wt . % gadolinium increases slightly the temperature of the a → y polymorphic trans- formation of iron ...
... alloys containing up to 5 wt . % Gd , which had been forged at 800 ° -900 ° into square 5 x5 mm rods . The addition of up to 3 wt . % gadolinium increases slightly the temperature of the a → y polymorphic trans- formation of iron ...
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
acid Akad alcohol alkali alloys aluminium ammonia ammonium anion aqueous solution Blagorod bromide cadmium caesium calculated carbonate cerium Chem chemical chloride coefficient complex ion composition concentration copper corresponding cristobalite crystallisation crystals decomposition determined dissociation electrode equilibrium diagram ether ethyl eutectic formation formed gallium glauberite H₂O H₂SO heating curve hydrogen hydroxide increase indium Inorg Inst instability constant ionic strength isotherms K₂SO Khim ligands liquid lithium melting metal method molar ratio molar volumes mole molecules MTPC Na₂SO NaCl Nauk SSSR neodymium Neorg nitrate nitrilotriacetic acid NO₂ Obshch obtained oxide platinum Platiny Drug polyhalite potassium praseodymium precipitate prepared pyridine reaction reagent refractive refractive indices Russ salt saturated shows sodium solid phase solid solutions solubility solvents stability studied sulphate sulphide Table temperature thallium tin selenide tion titanium trans effect uranyl values X-ray Zhur zinc zirconium