... alloys decreases as the Ag concentra- tion rises ( Fig . 4a ) . The hardness of the alloys quenched from 1200 ° passes through a clearly defined maximum ; this is presumably due to age - hardening since the alloy lies near the boundary ...
... alloys decreases as the Ag concentra- tion rises ( Fig . 4a ) . The hardness of the alloys quenched from 1200 ° passes through a clearly defined maximum ; this is presumably due to age - hardening since the alloy lies near the boundary ...
Trang 835
... alloys . The transforma- tion from the homogeneous into the heterogeneous region is not shown . The maximum on the hardness curve is attri- butable to the alloy Ag 5 , Pd 80 , Rh 15 wt . % , which lies near the boundary of the ẞ - solid ...
... alloys . The transforma- tion from the homogeneous into the heterogeneous region is not shown . The maximum on the hardness curve is attri- butable to the alloy Ag 5 , Pd 80 , Rh 15 wt . % , which lies near the boundary of the ẞ - solid ...
Trang 1076
... alloys , prepared from a hardener alloy , did not lose more than 0.1-0.2 % Ce , whereas the higher cerium alloys , prepared from the pure components , lost 2-3 % Ce . a , kX A 8.9 9.4 40420 408 0818 4,0400 500 14 4,5 a 40380 40360 b 95 ...
... alloys , prepared from a hardener alloy , did not lose more than 0.1-0.2 % Ce , whereas the higher cerium alloys , prepared from the pure components , lost 2-3 % Ce . a , kX A 8.9 9.4 40420 408 0818 4,0400 500 14 4,5 a 40380 40360 b 95 ...
Nội dung
Journal | 767 |
A P KOCHETKOVA V G TRONEV and O N GILYAROV | 811 |
1671 855 | 836 |
Bản quyền | |
4 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
acid Akad alcohol alkali alloys aluminium ammonia ammonium analysis anion aqueous solution Blagorod bromide cadmium caesium calculated carbonate cerium Chem chemical chloride cobalt coefficient complex ion composition concentration corresponding cristobalite crystallisation crystals CuCl decomposition determined dissociation electrode equilibrium diagram ether ethyl eutectic formation formed gallium glauberite H₂O heating curve hydrogen hydroxide increase indium Inorg Inst instability constant ionic strength isotherms Khim ligands liquid lithium melting metal method molar volumes mole molecules MTPC Na₂SO₄ NaCl Nauk SSSR neodymium Neorg NH NH nitrate nitrilotriacetic acid Obshch obtained oxide platinum Platiny Drug polyhalite potassium praseodymium precipitate prepared pyridine reaction reagent refractive refractive indices Russ salt saturated shows sodium solid phase solid solutions solubility solvents stability studied sulphate sulphide Table temperature thallium thermal TiCl4 tin selenide tion titanium trans effect uranyl values X-ray Zhur zinc zirconium