Russian Journal of Inorganic Chemistry, Tập 43,Số phát hành 9-12British Library Lending Division with the cooperation of the Royal Society of Chemistry, 1998 |
Từ bên trong sách
Kết quả 1-3 trong 91
Trang 1479
... patterns of mixtures of barium per- oxide with ( a ) titanium , ( b ) zirconium , ( c ) molybdenum , and ( d ) aluminum after 5 min of mechanical activation : ( 1 ) BaZrO3 , BaMoO4 ; and ( 2 ) Mo. resolved shoulder at 700-500 cm ( Fig ...
... patterns of mixtures of barium per- oxide with ( a ) titanium , ( b ) zirconium , ( c ) molybdenum , and ( d ) aluminum after 5 min of mechanical activation : ( 1 ) BaZrO3 , BaMoO4 ; and ( 2 ) Mo. resolved shoulder at 700-500 cm ( Fig ...
Trang 1480
... patterns , suggesting a fairly high crystallinity of the mechanochemically prepared product . Similar patterns were obtained from other mixed oxides , with minor dif- ferences in micrograin sizes . CONCLUSION This study shows that ...
... patterns , suggesting a fairly high crystallinity of the mechanochemically prepared product . Similar patterns were obtained from other mixed oxides , with minor dif- ferences in micrograin sizes . CONCLUSION This study shows that ...
Trang 1484
... patterns and Bragg peak positions are shown in Fig . 3. The experimental pattern coincides Intensity , impulse × 104 well with the simulated one and does not exhibit reflec- tions of other phases . RESULTS AND DISCUSSION In the ...
... patterns and Bragg peak positions are shown in Fig . 3. The experimental pattern coincides Intensity , impulse × 104 well with the simulated one and does not exhibit reflec- tions of other phases . RESULTS AND DISCUSSION In the ...
Nội dung
Synthesis and Properties of Inorganic Compounds | 1301 |
Xray Diffraction Study of LnMn2O5 5 Ln La Nd M Ca Ba LIBRARY | 1308 |
Synthesis of MolybdenumIV Oxide in Lithium ChloridePotassium Chloride EutecticMelts | 1317 |
Bản quyền | |
67 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption according acid addition analysis angle anions aqueous atoms band bond bridging calculated cation changes charge Chem chemical Chemistry chloride cm-¹ complexes composition compounds concentration constant containing coordination Copyright corresponding crystal curves decomposition decrease derivatives described determined diagram distances effect electron energy enthalpies experimental extraction formation frequencies H₂O heating higher hydrogen increase indicates initial Inorganic intensity interaction ions Khim kJ/mol ligand measured melt metal method mixed mixture mol/l molecules Moscow Neorg observed obtained occur oxide oxygen parameters phase phosphate positions powder prepared presented properties Publishing range ratio reaction REFERENCES region respectively Russian salts samples shift shows similar sodium solid solution space group spectra spectrum stability structure studied synthesis Table temperature thermal tion Translation unit values vibrations X-ray diffraction